Improvement of the multilayer morphology (alumina/Cu/YIG/Cu) to characterize YIG thin film

Abstract : The aim of our study is to characterize yttrium iron garnet (YIG) thin film for its applications in the microwaves and magnetooptical domains. For this purpose, we have manufactured a microinductor by deposition of YIG film between two copper layers on an alumina substrate. Multilayers have been deposited by radio-frequency magnetron sputtering technique. Thin films of YIG are amorphous after deposition; a post-thermal annealing at 740 8C for 2 h is necessary to obtain satisfactory magnetic properties. In this work, we have studied the effects of different parameters concerning the substrate surface state, deposition and post-thermal treatment of YIG and copper thin films on their structure and morphological properties. We have come against several mechanical and electrical problems: crack formation, detachment of YIG or Cu films from the substrate, deterioration of Cu films, open or short circuits. The roughness of alumina substrate and the annealing mode play an important role on the quality of themicroinductor prototype. After several tests by varying different parameters, we have established a protocol permitting to manufacture a prototype of good quality. This prototype is characterized using: profilometry, scanning electron microscopy, X-ray diffraction, vibrating sample magnetometry, and a precision LCR meter.
Keywords : thin films YiG
Type de document :
Article dans une revue
physica status solidi (a), Wiley, 2011, 208 (7), pp.1678-1682. 〈10.1002/pssa.201026511〉
Liste complète des métadonnées
Contributeur : Jean-Pierre Chatelon <>
Soumis le : jeudi 14 février 2013 - 17:07:47
Dernière modification le : dimanche 15 octobre 2017 - 22:44:13

Lien texte intégral




Ismail Khalil, A. Siblini, Jean-Pierre Chatelon, M.-F. Blanc-Mignon, Jean-Jacques Rousseau. Improvement of the multilayer morphology (alumina/Cu/YIG/Cu) to characterize YIG thin film. physica status solidi (a), Wiley, 2011, 208 (7), pp.1678-1682. 〈10.1002/pssa.201026511〉. 〈ujm-00788613〉



Consultations de la notice